Penurunan intensitas zat warna sintetis menggunakan komposit SiO2/ZnO dari sekam padi dan limbah baterai

Listiani, Popy (2018) Penurunan intensitas zat warna sintetis menggunakan komposit SiO2/ZnO dari sekam padi dan limbah baterai. Diploma thesis, UIN Sunan Gunung Djati Bandung.

[img]
Preview
Text (COVER)
1_COVER.pdf

Download (50kB) | Preview
[img]
Preview
Text (ABSTRAK)
2_ABSTRAK.pdf

Download (142kB) | Preview
[img]
Preview
Text (DAFTAR ISI)
3_DAFTAR ISI.pdf

Download (138kB) | Preview
[img]
Preview
Text (BAB I)
4_BAB I.pdf

Download (128kB) | Preview
[img] Text (BAB II)
5_BAB II.pdf
Restricted to Registered users only

Download (399kB) | Request a copy
[img] Text (BAB III)
6_BAB III.pdf
Restricted to Registered users only

Download (200kB) | Request a copy
[img] Text (BAB IV)
7_BAB IV.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text (BAB V)
8_BAB V.pdf
Restricted to Registered users only

Download (106kB) | Request a copy
[img] Text (DAFTAR PUSTAKA)
9_DAFTAR PUSTAKA.pdf
Restricted to Registered users only

Download (128kB) | Request a copy

Abstract

Melimpahnya jumlah sekam padi dan limbah baterai di Indonesia membutuhkan pengolahan lebih lanjut, sekam padi berpotensi sebagai sumber SiO2 sedangkan limbah baterai berpotensi sebagai sumber ZnO. Sintesis komposit SiO2/ZnO dari kedua bahan tersebut berpotensi sebagai fotokatalis untuk mengurangi intensitas zat warna dalam limbah di perairan. Penelitian ini bertujuan untuk mensintesis komposit SiO2/ZnO untuk menurunkan intensitas zat warna Methylene Blue dan Rhodamin B. Komposit SiO2/ZnO disintesis dengan metode sol gel pada perbandingan mol SiO2:ZnO sebesar 4:1, 1:1, 1:4, 1:8, dan 1:16. Setelah dikarakterisasi menggunakan XRD, partikel SiO2 yang dihasilkan merupakan mineral cristobalite sedangkan partikel ZnO yang dihasilkan merupakan mineral zincite. Data SEM menunjukkan bahwa morfologi kristal komposit SiO2/ZnO berupa bongkahan dengan ukuran yang tidak seragam, serta terdapat aglomerasi partikel. Komposit SiO2/ZnO hasil sintesis dapat menurunkan intensitas zat warna Methylene Blue dan Rhodamin B dengan menggunakan sinar UV. Pada aplikasi komposit SiO2/ZnO terhadap dekolorisasi Methylene Blue dan Rhodamin B dilakukan juga variasi massa komposit, variasi waktu penyinaran, variasi konsentrasi larutan, dan variasi sumber cahaya. Persen dekolorisasi terbesar yang dihasilkan pada larutan Methylene Blue yaitu 98,19% menggunakan komposit 1:4 sebanyak 0,15 gram terhadap 25 mL larutan Methylene Blue 10 ppm, sedangkan persen dekolorisasi terbesar pada larutan Rhodamin B yaitu 89,06% menggunakan komposit 1:4 sebanyak 0,15 gram terhadap 25 mL larutan Rhodamin B 3,5 ppm. The abundance of rice husks and battery waste in Indonesia requires further processing, rice husks have the potential to be a source of SiO2, while battery waste has the potential to be a source of ZnO. The synthesis of SiO2/ZnO composites from these two materials has the potential as photocatalysts for reducing the intensity of dyes in wastes in the waters. This study aims to synthesis SiO2/ZnO composites to reduce the intensity of Methylene Blue and Rhodamin B. SiO2/ZnO composites were synthesized by sol gel method at SiO2:ZnO mole ratio of 4:1, 1:1, 1:4, 1:8, and 1:16. After being characterized using XRD, the resulting SiO2 particles are cristobalite, while minerals ZnO particles produced are zincite minerals. SEM data shows that the SiO2/ZnO composite crystal morphology is in the form of lumps with a non-uniform size, and there are particle agglomerations. The synthesized SiO2/ZnO composite can reduce the intensity of Methylene Blue and Rhodamin B dyes using UV light. In SiO2/ZnO composite application for decolorization of Methylene Blue and Rhodamine B, composite mass variations, irradiation time variations, variations in solution concentration, and variations in light sources were carried out. The biggest decolorization percentage produced in Methylene Blue solution is 98.19% using 1:4 composite as much as 0.15 grams to 25 mL of 10 ppm Methylene Blue solution, while the biggest percent decolorization in Rhodamin B solution is 89.06% using composite 1: 4 0.15 grams of 25 mL of Rhodamin B 3.5 ppm.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: komposit SiO2/ZnO; adsorpsi; fotokatalisis; sekam padi; limbah baterai; Methylene Blue; Rhodamin B;
Subjects: Inorganic Chemistry
Ecology > Environmental Chemistry
Divisions: Fakultas Sains dan Teknologi > Program Studi Kimia
Depositing User: Popy Listiani
Date Deposited: 10 Dec 2018 05:21
Last Modified: 10 Dec 2018 05:21
URI: http://digilib.uinsgd.ac.id/id/eprint/14826

Actions (login required)

View Item View Item