Recovery Oksida Mangan dan Oksida Zink dari Limbah Baterai dengan metoda Hidrometalurgi untuk Aplikasi Fotodegradasi Zat Warna Metilen Biru

Pratiwi, Restiani Alia (2018) Recovery Oksida Mangan dan Oksida Zink dari Limbah Baterai dengan metoda Hidrometalurgi untuk Aplikasi Fotodegradasi Zat Warna Metilen Biru. Diploma thesis, UIN Sunan Gunung Djati Bandung.

[img]
Preview
Text (COVER)
1_cover.pdf

Download (172kB) | Preview
[img]
Preview
Text (ABSTRAK)
2_abstrak.pdf

Download (164kB) | Preview
[img]
Preview
Text (DAFTAR ISI)
3_daftarisi.pdf

Download (171kB) | Preview
[img]
Preview
Text (BAB I)
4_bab1.pdf

Download (285kB) | Preview
[img] Text (BAB II)
5_bab2.pdf
Restricted to Registered users only

Download (823kB) | Request a copy
[img] Text (BAB III)
6_bab3.pdf
Restricted to Registered users only

Download (328kB) | Request a copy
[img] Text (BAB IV)
7_bab4.pdf
Restricted to Registered users only

Download (680kB) | Request a copy
[img] Text (BAB V)
8_bab5.pdf
Restricted to Registered users only

Download (161kB) | Request a copy
[img] Text (DAFTAR PUSTAKA)
9_daftarpustaka.pdf
Restricted to Registered users only

Download (170kB) | Request a copy

Abstract

INDONESIA: Komponen penyusun utama pada baterai yaitu pasta. Pasta pada limbah baterai mengandung logam berat, terutama logam Mn dan Zn. Logam berat ini memiliki sifat tahan urai yang menyebabkan logam terakumulasi dalam perairan. Logam berat yang masuk ke dalam perairan dapat masuk ke dalam tubuh manusia secara langsung maupun tidak langsung. Maka dari itu perlu dilakukan pengolahan limbah baterai untuk meminimalisir pencemaran lingkungan karena logam berat. Metilen biru merupakan salah satu limbah zat warna yang dihasilkan dari industri. Metilen biru merupakan senyawa organik berwarna yang sulit terurai di lingkungan. Salah satu metode pengolahan limbah zat warna yang dapat dilakukan untuk mengurangi pencemaran lingkungan yaitu fotokatalisis. Pada penelitian ini digunakan metoda hidrometalurgi untuk recovery Oksida Mangan dan Oksida Zink dari pasta limbah baterai. Pasta diberi perlakuan pencucian dengan akua dm, dan pencucian dengan H2SO4 0,5 M. Digunakan agen pereduksi H2O2 30% untuk membantu melarutkan Mn. Mn dan Zn kemudian dipisahkan dengan cara presipitasi pada pH 13 untuk mengendapkan Mn kemudian dibuat pH 10 untuk mengendapkan Zn. Setelah itu dilakukan karakterisasi XRD dan XRF. Produk Mn2O3 dan ZnO yang didapat kemudian diaplikasikan pada proses dekolorisasi zat warna Metilen biru sebagai fotokatalis. Didapatkan % recovery untuk Mn sebesar 66,8% dan Zn sebesar 67,9%. Produk Mn dan Zn dapat menurunkan intensitas zat warna Metilen Biru dengan menggunakan sinar UV dan cahaya matahari. Hasil % dekolorisasi terbesar yang dihasilkan pada larutan Metilen Biru dengan sinar UV yaitu 38,85% dan dengan cahaya matahari sebesar 85,41%. ENGLISH: The main constituent component of the battery is pasta. Pasta in battery waste contains heavy metals, especially Mn and Zn metals. This heavy metal has breakdown properties which causes metals to accumulate in the waters. Heavy metals that enter the waters can enter directly into the human body directly or indirectly. Therefore it is necessary to process battery waste to minimize environmental pollution due to heavy metals. Methylene blue is one of the waste dyes produced from industry. Methylene blue is a colored organic compound that is difficult to decompose in the environment. One method of processing waste dyes that can be done to reduce environmental pollution is photocatalysis. In this study hydrometallurgical methods for the recovery of Manganese Oxide and Zink Oxide from battery waste pastes were used. Pasta was treated with washing with aqua dm, and washing with 0.5 M H2SO4. H2O2 30% reducing agent was used to help dissolve Mn. Mn and Zn are then separated by precipitation at pH 13 to precipitate Mn then made pH 10 to precipitate Zn. After that XRD and XRF characterization was carried out. The Mn2O3 and ZnO products obtained were then applied to the decolorization process of the dye Methylene blue as a photocatalyst. Obtained% recovery for Mn of 66.8% and Zn of 67.9%. Mn and Zn products can reduce the intensity of Methylene Blue dyes using UV light and sunlight. The biggest% decolorization results were produced in Methylene Blue solution with UV light which was 38.85% and with sunlight at 85.41%.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Oksida Mangan; Oksida Zink; Fotokatalisis; Limbah Baterai; Metilen Biru
Subjects: Science and Religion
Chemistry and Allied Science > Data Processing and Analysis of Chemistry
Analytical Chemistry > Qualitative Analysis, Quantitavie Analysis of Chemistry
Divisions: Fakultas Sains dan Teknologi > Program Studi Kimia
Depositing User: Restiani Alia Pratiwi
Date Deposited: 29 Jan 2019 03:52
Last Modified: 29 Jan 2019 03:52
URI: http://digilib.uinsgd.ac.id/id/eprint/18394

Actions (login required)

View Item View Item