Pemanfaatan pasir Besi Alam sebagai Bahan Baku pembuatan Magnet Permanen Barium Heksaferit (BaFe12O19)

Muslim, Husni Taufiq (2016) Pemanfaatan pasir Besi Alam sebagai Bahan Baku pembuatan Magnet Permanen Barium Heksaferit (BaFe12O19). Diploma thesis, UIN Sunan Gunung Djati Bandung.

[img]
Preview
Text (COVER)
1_COVER.pdf

Download (223kB) | Preview
[img]
Preview
Text (ABSTRAK)
2_ABSTRAK.pdf

Download (305kB) | Preview
[img]
Preview
Text (DAFTAR ISI)
3_DAFTAR ISI.pdf

Download (306kB) | Preview
[img]
Preview
Text (BAB I)
4_BAB I.pdf

Download (317kB) | Preview
[img] Text (BAB II)
5_BAB II.pdf
Restricted to Registered users only

Download (734kB)
[img] Text (BAB III)
6_BAB III.pdf
Restricted to Registered users only

Download (674kB)
[img] Text (BAB IV)
7_BAB IV.pdf
Restricted to Registered users only

Download (1MB)
[img] Text (BAB V)
8_BAB V.pdf
Restricted to Registered users only

Download (301kB)
[img] Text (DAFTAR PUSTAKA)
9_DAFTAR PUSTAKA.pdf
Restricted to Registered users only

Download (199kB)

Abstract

INDONESIA Sintesis material magnet BaFe12O19 dengan pemanfaatan pasir besi alam sebagai bahan baku telah berhasil dilakukan. Penelitian ini bertujuan untuk mengetahui sifat magnet yang dihasilkan oleh bahan baku pasir besi alam yang telah diproses menjadi hematit (α-Fe2O3) dengan menghilangkan impurities dengan cara pemurnian roasting dan pemurnian oleh HCl. Karakterisasi dilakukan dengan menggunakan Permagraph C, SEM, EDS dan Gaussmeter untuk mengetahui sifat magnet permanen, struktur morfologi, komposisi senyawa hasil sintesis dan besar nilai gauss yang terbentuk pada material magnet BaFe12O19. Hasil karakterisasi menunjukkan sifat magnet sampel terbaik pada pemurnian HCl, yaitu induksi remanen sebesar 0,52 kG, koersivitas sebesar 0,753 kOe dan nilai kuat medan magnet permukaan sebesar 110 G, serta memiliki struktur heksagonal dengan persen massa tiap senyawa yang terbentuk 29,28% BaO dan 70,72% FeO. ENGLISH Synthesis of magnet materials BaFe12O19 using natural iron ore as raw material has been succesfully. This study aims to determine magnetic properties by natural iron ore have been processed into hematite (α-Fe2O3) by eliminating impurities with roasting purification and HCl purification. Characterization was performed using Permagraph C, SEM, EDS and Gaussmeter to determine magnetic properties, structure morphology, composition of compound synthesized and the value of Gauss magnetic material formed on BaFe12O19. The results show magnetic properties of the best samples by HCl purification is 0,52 kG remanent induction, 0,753 kOe of coercivity and 110 G of strong magnetic field, and has a hexagonal structure with the mass percent of each compound 29,28% BaO and 70,72% FeO.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Pasir besi alam; material BaFe12O19; stuktur heksagonal;
Subjects: Physics > Miscellany of Physics
Modern Physics > Atomic and Nuclear Physics
Divisions: Fakultas Sains dan Teknologi > Program Studi Fisika
Depositing User: rofita fita robi'in
Date Deposited: 20 Feb 2019 03:31
Last Modified: 20 Feb 2019 03:31
URI: http://digilib.uinsgd.ac.id/id/eprint/18652

Actions (login required)

View Item View Item