Sintesis grafena (rGO) dari arang tempurung kelapa (cocos nucifera)

Hidayat, Ahmad (2017) Sintesis grafena (rGO) dari arang tempurung kelapa (cocos nucifera). Diploma thesis, UIN Sunan Gunung Djati Bandung.

[img]
Preview
Text (COVER)
1_COVER.pdf

Download (197kB) | Preview
[img]
Preview
Text (ABSTRAK)
2_ABSTRAK.pdf

Download (404kB) | Preview
[img]
Preview
Text (DAFTAR ISI)
3_DAFTAR ISI.pdf

Download (196kB) | Preview
[img]
Preview
Text (BAB I)
4_BAB I.pdf

Download (309kB) | Preview
[img] Text (BAB II)
5_BAB II.pdf
Restricted to Registered users only

Download (756kB)
[img] Text (BAB III)
6_BAB III.pdf
Restricted to Registered users only

Download (318kB)
[img] Text (BAB IV)
7_BAB IV.pdf
Restricted to Registered users only

Download (636kB)
[img] Text (BAB V)
8_BAB V.pdf
Restricted to Registered users only

Download (300kB)
[img] Text (DAFTAR PUSTAKA)
9_DAFTAR PUSTAKA.pdf
Restricted to Registered users only

Download (332kB)

Abstract

INDONESIA : Grafena merupakan satu lapis atom karbon yang memiliki hibridisasi sp2 membentuk struktur heksagonal 2D. Grafena memiliki potensi yang sangat luas termasuk nanoelectronic materials. Penelitian ini bertujuan untuk mensintesis grafena (rGO) dari arang tempurung kelapa dengan menggunakan metode modifikasi Hummer. Modifikasi dilakukan dengan menghilangkan NaNO3. Sintesis dilakukan dengan ukuran partikel grafit sebesar 50 μm dan waktu oksidasi selama 5 hari. Analisis gugus fungsi dan struktur grafena (rGO) dilakukan dengan pengujian FTIR dan XRD. Hasil pengujian FTIR menunjukan adanya puncak pada panjang gelombang 1604,8919 cm-1 dari ikatan C=C aromatik yang merupakan indikasi terbentuknya grafena (rGO). Hasil pengujian UV-Vis menunjukan adanya serapan pada panjang gelombang 272 cm-1 yang disebabkan oleh transisi π→π ⃰ dari ikatan C=C pada cincin aromatik. Pengujian XRD menghasilkan puncak difraktogram pada sudut 2θ 24° yang khas untuk material grafena (rGO). ENGLISH : Graphene is a single layer of carbon atoms that have sp2 hybridization to form a 2D hexagonal structure. Graphene wich have very widely potential including nanoelectronic materials. This study aims to synthesize graphene (rGO) from coconut shell charcoal using a modified Hummer. Modifications done by eliminating NaNO3. Synthesis is done with graphite particle size of 50 μm and oxidation time for 5 days. Analysis of the functional groups and the structure of graphene (rGO) is done by testing FTIR, UV-Vis, and XRD. FTIR test results showed a peak at a wavelength 1604.8919 cm-1 of the C=C aromatic which is indicative of the formation of graphene (rGO). UV-Vis test result showed a absorption peak at 272 cm-1, which is attributed to the π→π ⃰ of the C=C bond from aromatic rings. Testing XRD diffractogram produces a peak 2θ at 24 ° are typical for the material graphene (rGO).

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Modifikasi Hummer ; sintesis; material; grafit;
Subjects: Chemistry and Allied Science > Data Processing and Analysis of Chemistry
Divisions: Fakultas Sains dan Teknologi > Program Studi Kimia
Depositing User: rofita fita robi'in
Date Deposited: 09 Oct 2019 02:26
Last Modified: 09 Oct 2019 02:26
URI: http://digilib.uinsgd.ac.id/id/eprint/24772

Actions (login required)

View Item View Item