Optimasi pemisahan TiO2 dari pasir besi pantai Sukabumi Selatan menggunakan proses leaching asam klorida dengan reduktor Fe0

Panem, Muhammad Burhanudin (2016) Optimasi pemisahan TiO2 dari pasir besi pantai Sukabumi Selatan menggunakan proses leaching asam klorida dengan reduktor Fe0. Diploma thesis, UIN Sunan Gunung Djati Bandung.

[img]
Preview
Text (COVER)
1_COVER.pdf

Download (210kB) | Preview
[img]
Preview
Text (ABSTRAK)
2_ABSTRAK.pdf

Download (296kB) | Preview
[img]
Preview
Text (DAFTAR ISI)
3_DAFTAR ISI.pdf

Download (495kB) | Preview
[img]
Preview
Text (BAB I)
4_BAB I.pdf

Download (205kB) | Preview
[img] Text (BAB II)
5_BAB II.pdf
Restricted to Registered users only

Download (432kB)
[img] Text (BAB III)
6_BAB III.pdf
Restricted to Registered users only

Download (313kB)
[img] Text (BAB IV)
7_BAB IV.pdf
Restricted to Registered users only

Download (597kB)
[img] Text (BAB V)
8_BAB V.pdf
Restricted to Registered users only

Download (195kB)
[img] Text (DAFTAR PUSTAKA)
9_DAFTAR PUSTAKA.pdf
Restricted to Registered users only

Download (427kB)

Abstract

INDONESIA : Pasir besi merupakan salah satu bahan baku untuk memproduksi titanium dioksida karena mineral utama penyusunnya adalah magnetit (Fe3O4), ilmenit (FeTiO3) dan hematit (Fe2O3). Berdasarkan hasil karakterisasi dengan XRF (X-Ray Fluorescence) diketahui persentase TiO2 pada pantai Sukabumi Selatan sebesar 24,22 %. Pada penelitian ini TiO2 diperoleh dari estraksi pasir besi dengan metode leaching HCl di mana konsentrasi HCl dioptimasi yaitu 4 M, 6 M dan 8 M. sebelum dicampurkan dengan HCl, pasir besi ukuran 100 mesh melewati tahap pra-oksidasi yaitu dengan cara dikalsinasi pada suhu 700 °C. Campuran pasir besi dengan HCl dicampurkan serbuk Fe0 sebagai reduktor untuk meningkatkan oksidasi pada reaksi pengendapan TiO2. Berdasarkan hasil XRF produk leaching HCl disimpulkan bahwa konsentrasi HCl optimum adalah 6 M dengan persentasi TiO2 terbesar yaitu 76,73 %. ENGLISH : Iron sand can be the one of a raw material for producing titanium dioxide as the main constituent minerals are magnetite (Fe3O4), ilmenite (FeTiO3) and hematit (Fe2O3). Based on the results of characterization by XRF (X-Ray Fluorescence) known percentage of TiO2 in iron sand of South Coast Sukabumi is 24.22%. In this study, TiO2 obtained from extraction of iron sand by leaching using HCl which the concentration of HCl is optimized 4 M, 6 M and 8 M. before mixed with HCl, iron sand 100 mesh pass pre-oxidation stage that is by calcined at a temperature of 700 ° C , iron sand mixture with HCl and Fe0 powder as a reducing agent to enhance the deposition of TiO2 oxidation reaction. Based on the results of XRF on leaching HCl product concluded that the optimum concentration was 6 M HCl with the largest percentage of TiO2 is 76.73%.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: TiO2; pasir besi; leaching; XRF.;
Subjects: Chemistry and Allied Science > Data Processing and Analysis of Chemistry
Ecology > Environmental Chemistry
Divisions: Fakultas Sains dan Teknologi > Program Studi Kimia
Depositing User: rofita fita robi'in
Date Deposited: 04 Jul 2019 04:22
Last Modified: 04 Jul 2019 04:22
URI: https://digilib.uinsgd.ac.id/id/eprint/21208

Actions (login required)

View Item View Item