Stiara, Ramdan Gungun (2016) Sintesis zeolit fau dan optimasinya dari abu gosok dan kaleng minuman berkarbonasi. Diploma thesis, UIN Sunan Gunung Djati Bandung.
|
Text (COVER)
1_COVER.pdf Download (206kB) | Preview |
|
|
Text (ABSTRAK)
2_ABSTRAK.pdf Download (409kB) | Preview |
|
|
Text (DAFTAR ISI)
3_DAFTAR ISI.pdf Download (204kB) | Preview |
|
|
Text (BAB I)
4_BAB IPENDAHULUAN.pdf Download (314kB) | Preview |
|
![[img]](https://digilib.uinsgd.ac.id/style/images/fileicons/text.png) |
Text (BAB II)
5_BAB IITINJAUAN PUSTAKA.pdf Restricted to Registered users only Download (801kB) |
|
|
Text (BAB III)
6_BAB IIIMETODE PENELITIAN.pdf Restricted to Registered users only Download (417kB) |
|
|
Text (BAB IV)
7_BAB IVHASIL PENELITIAN DAN PEMBAHASAN.pdf Restricted to Registered users only Download (594kB) |
|
|
Text (BAB V)
8_BAB V KESIMPULAN DAN SARAN.pdf Restricted to Registered users only Download (304kB) |
|
|
Text (DAFTAR PUSTAKA)
9_DAFTAR PUSTAKA.pdf Restricted to Registered users only Download (317kB) |
Abstract
INDONESIA Abu gosok memiliki kadar silika mencapai 80,25% yang sangat berpotensi digunakan sebagai sumber silika untuk sintesis zeolit. Pada penelitian ini abu gosok langsung dicampurkan sebagai bahan sintesis. Optimasi sintesis dilakukan dengan variasi 1) 18 jam aging dengan 30 jam inkubasi, 2) 36 jam aging dengan 24 jam inkubasi dan 3) 18 jam aging dengan 24 jam inkubasi. Sintesis Zeolit FAU menggunakan metode non-hidrotermal pada suhu 90℃. Hasil analisa XRD menunjukkan ketiga variasi sintesis terbentuk zeolit FAU, namun 1) 24 jam aging dengan 30 jam inkubasi dan 2) 36 jam aging dengan 24 jam inkubasi menunjukan kristalinitas yang lebih baik. Hasil analisis SEM diperoleh morfologi permukan seperti kubus yang menumpuk dengan ukuran partikel sekitar 1-1,6 µm. ENGLISH Rice husk ash has silica content approximately 85,25% that was quite potential to be used as silica source for zeolite synthesis. In the research rice husk ash direct used as material synthesis. Optimation synthesis in variation 1) 18 hours aging with 30 hours incubation , 2) 36 hours aging with 24 hours incubation dan 3) 18 hours aging with 24 hours incubation. Synthesis of FAU zeolite by non-hidrothermal method at temperature of 90 ℃. The result of XRD showed third variation formed zeolite FAU, however 1) 24 hours aging with 30 hours incubation and 2) 36 hours aging with 24 hours incubation indicate optimum crystal. Result of the analysis by SEM of FAU zeolite showed surface accidance as sixangel pile up with different size about 1-1,6 μm.
| Item Type: | Thesis (Diploma) |
|---|---|
| Uncontrolled Keywords: | abu gosok; zeolit FAU; non-hidrotermal; optimasi zeolit; waktu aging; waktu inkubasi; |
| Subjects: | Chemistry and Allied Science > Data Processing and Analysis of Chemistry |
| Divisions: | Fakultas Sains dan Teknologi > Program Studi Kimia |
| Depositing User: | rofita fita robi'in |
| Date Deposited: | 25 Apr 2019 02:59 |
| Last Modified: | 25 Apr 2019 03:02 |
| URI: | https://digilib.uinsgd.ac.id/id/eprint/19937 |
Actions (login required)
 |
View Item |