Isolasi Alginat Dari Biomassa Alga Cokelat (Sargassum sp) Untuk Adsorpsi Ion Logam Timbal(II)

Mu'adi, Lutfi (2017) Isolasi Alginat Dari Biomassa Alga Cokelat (Sargassum sp) Untuk Adsorpsi Ion Logam Timbal(II). Diploma thesis, UIN Sunan Gunung Djati Bandung.

Preview	Text (COVER) 1_Cover.pdf Download (175kB) | Preview
Preview	Text (ABSTRAK) 2_Abstrak.pdf Download (103kB) | Preview
Preview	Text (DAFTAR ISI) 3_Daftar Isi.pdf Download (153kB) | Preview
Preview	Text (BAB I) 4_Bab I.pdf Download (168kB) | Preview
	Text (BAB II) 5_Bab II.pdf Restricted to Registered users only Download (798kB) | Request a copy
	Text (BAB III) 6_Bab III.pdf Restricted to Registered users only Download (436kB) | Request a copy
	Text (BAB IV) 7_Bab IV.pdf Restricted to Registered users only Download (876kB) | Request a copy
	Text (BAB V) 8_Bab V.pdf Restricted to Registered users only Download (210kB) | Request a copy
	Text (DAFTAR PUSTAKA) 9_Daftar Pustaka.pdf Restricted to Registered users only Download (197kB) | Request a copy

Abstract

Pada penelitian ini dilakukan adsorpsi ion logam timbal(II) dengan menggunakan adsorben Na-alginat hasil ekstraksi dari biomassa alga cokelat Sargassum sp. Dari hasil ekstraksi Na-alginat dikarakterisasi FT-IR dengan menunjukan gugus fungsi yang terkandung pada alginat yaitu adanya gugus aktif pada Na-alginat yaitu gugus hidroksil pada bilangan gelombang 3448,72 cm-1, gugus karboksil pada bilangan gelombang 1778,37 cm-1, gugus karbonil pada bilangan gelombang 1639,49 cm-1, dan gugus khas penyusun Na-alginat yaitu gugus Na dalam isomer alginat pada bilangan gelombang 1440 cm-1, C-O-C glikosidik pada bilangan gelombang 1332,81 cm-1 dan C-H khas piranosa pada bilangan gelombang 879,54 cm-1. Kemudian dikarakterisasi SEM untuk mengetahui morfologi pada adsorben Na-alginat dan pori-pori pada struktur alginat. Agar didapatkan kondisi adsorpsi yang optimum dilakukan optimasi pH, waktu kontak, konsentrasi adsorpsi dengan menggunakan metode batch dan kinerja analitik adsorpsi-desorpsi dengan menggunakan metode kolom. Dari hasil optimasi dihasilkan pH optimum adalah di pH 5, waktu kontak 30 menit, dan konsentrasi 30 ppm. Pada metode kolom proses kinerja analitik adsorpsi-desorpsi dihasilkan persen perolehan > 90% daya serap adsoben Na-alginat terhadap ion logam timbal(II). Dari hasil penelitian, hasil ekstraksi alga cokelat Sargassum sp dihasilkan senyawa Na-alginat sehingga merupakan adsorben yang baik untuk menyerap ion logam timbal(II). Dibuktikan dengan hasil efisiensi penyerapan optimum terhadap ion logam timbal(II) sebesar 95,16% dan hasil kapasitas adsorpsi optimum sebesar 10,5950 mg/g. In this research, the adsorption of lead metal ions (II) by using Na-alginate adsorbent extracted from Sargassum sp. Brown algae biomass. The result of Na-alginate extraction was characterized by FT-IR by showing functional groups contained in alginate, ie the presence of active group in Na-alginate, hydroxyl group at wave number 3448,72 cm-1, carboxyl group at wave number 1778,37 cm-1 , a carbonyl group of 1639,49 cm-1 waves, and a typical Na-alginate constituent group of Na groups in alginate isomers at 1440 cm-1 wave numbers, glycosidic C-O-C at wave numbers 1332,81 cm-1 and typical C-H piranose at wave number 879,54 cm-1. Then characterized SEM to determine the morphology of Na-alginate adsorbent and pores on alginate structure. In order to obtain optimum adsorption conditions, pH optimization, contact time, adsorption concentration by batch method and performance of adsorption-desorption adsorption using column method. The optimum result of optimum pH is pH 5, contact time 30 minutes, and concentration 30 ppm. In the adsorption-desorption process adsorption process column method, the percentage yield> 90% adsorption Na-alginate absorption capacity of lead metal ions (II). From the results of the research, the result of extraction of Sargassum sp brown algae is produced by Na-alginate compound so that it is a good adsorbent to absorb lead metal ions (II). It is proved that the optimum absorption result of lead metal (II) ion is 95,16% and the optimum adsorption capacity is 10,5950 mg /g.